  HL-93 potassium chloride zinc-plating additives B
HL-93 high cloud point potassium chloride zinc-plating brightening agent
Packing specifications: 25kg/plastic drum
200kg/plastic drum
1000kg/plastic drum on metal pallet
Â
The coating has high brightness, low brittleness, turbidity point of the bath can reach more than 80℃, and bright coating can be plated at 65℃. Its comprehensive performance can be completely comparable with similar foreign products, characteristics are as follows:
1. The bath does not contain ammonium, the wastewater is not polluted and easy to treat.
2. The coating is bright, suitable for low chromium passivation.
3. Adaptable to all kinds of basic materials, such as carbon steel, penetrant steel, cast iron, zinc pressure casting parts can be plated with bright zinc layer.
4. Coating brittleness is small, suitable for thicker zinc plating layer.
5. Additive consumption is low, plating solution maintenance is easy, conducive to reducing production costs.
6. The bath foam is low, both barrel and rack plating can be used.
7. Bath temperature range is wide.
Â
Â
 |
Concentration range |
Standard concentration |
KCl |
200-230 g/L |
220g/L |
ZnCl |
60-100 g/L |
60g/L (barrel) |
Boric Acid |
30-40 g/L |
35 g/L |
HL-93 Softening Agent |
20-30 g/L |
25 g/L |
HL-93 Brightening Agent |
0.6 ml/L- 1.0 ml/L |
0.8ml/L |
Temperature (℃) |
10-55℃ |
40℃ |
PH value |
4.8-5.6 |
5.2 |
DK (A/dm2) |
0.1-5 |
3 |
Â
Â
1. Add tap water with a total volume of 1/2 to the aqueduct, add the required amount of potassium chloride, and stir to dissolve it completely.
2. Dissolve the required amount of boric acid in hot water and add it to the tank. Then add zinc chloride and water to desired volume and stir until completely dissolved.
3. Add the required amount of HL-93 softener into the mix, and then add the required amount of HL-93 brightener into the plating solution for 2-3 times dilution, stir while adding, stir evenly, and check the PH value before electroplating.